Stress-Strain on Crystals
Posted 07.01.2010, 15:46 GMT-5 1 Reply
Please login with a confirmed email address before reporting spam
Hey,
I'm trying to find the young's modulus on a specific type of crystals. The material is not found in the list of materials that comsol has.
I was wondering if I can chemically make these crystals using another part of comsol (reaction or chemical engr. module), and then use them as the material for the structural-mechanic module.
Is that possible?
Thanks,
Ben
1 Reply Last Post 10.01.2010, 08:02 GMT-5
Please login with a confirmed email address before reporting spam
Posted:
2 decades ago
Hi
I beleive that would be rather complex, to model eveything from scratch in COMSOL, would be nice though.
I would search through the web and specially the litterature, either to find someone who has measured what you want, or has done some measurements where you can simulate the model correctly and then optimise the E/D values, but this requires many measurements in different directions as crystals are mostly anistropic. You must analyse/determine also the crystalline structure as this has an important effect on the stiffness matrix symmetry and the number of DoF's to resolve.
Finaly, you can get some guesses by similarity with other crystals, but you need to be a good and experienced material scientist then.
With anisotropic material do not forget to set up correctly your local coordinate frame in COMSOL
Good luck
Ivar
I beleive that would be rather complex, to model eveything from scratch in COMSOL, would be nice though.
I would search through the web and specially the litterature, either to find someone who has measured what you want, or has done some measurements where you can simulate the model correctly and then optimise the E/D values, but this requires many measurements in different directions as crystals are mostly anistropic. You must analyse/determine also the crystalline structure as this has an important effect on the stiffness matrix symmetry and the number of DoF's to resolve.
Finaly, you can get some guesses by similarity with other crystals, but you need to be a good and experienced material scientist then.
With anisotropic material do not forget to set up correctly your local coordinate frame in COMSOL
Good luck
Ivar